Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength

Nam Wook Kim

doi:doi:10.11648/j.jccee.20220706.11

| Peer-Reviewed

Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength

Nam Wook Kim

Published in Journal of Civil, Construction and Environmental Engineering (Volume 7, Issue 6)

Received: 20 October 2022 Accepted: 10 November 2022 Published: 8 December 2022

Views: Downloads:

Download PDF

Share This Article

Twitter
Linked In
Facebook

Abstract

The durability of concrete slabs is apt to be influenced by finishing methods and curing methods of concrete surface. Therefore, the finishing agent had better use in case of high strength concrete, the wet curing had better carry out on concrete surface. However, it is not obvious that when wet curing is started after finishing of concrete surface. In this study, the effects of the difference in finishing methods and curing methods on the surface properties of concrete were examined by surface tensile test, air permeability test, water absorption test and scaling test. As a result, use of the finishing agent was effective to improve the surface properties in high strength concrete. However, use of the finishing agent was ineffective in normal strength concrete. When wet curing was carried out, high strength concrete was more effective than normal strength concrete. The surface properties of concrete could be improved when the wet curing was begun after it passed for several hours from finale set of the setting time test for concrete. It is considered that, however, there is not much difference in surface quality within that range, and it is acceptable to start curing water the next day.

Published in	Journal of Civil, Construction and Environmental Engineering (Volume 7, Issue 6)
DOI	10.11648/j.jccee.20220706.11
Page(s)	102-108
Creative Commons	This is an Open Access article, distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution and reproduction in any medium or format, provided the original work is properly cited.
Copyright	Copyright © The Author(s), 2022. Published by Science Publishing Group

Keywords

Surface Quality, Curing Method, Strength, Finishing Method, Setting Time

References

[1]	Shumuye, E, D. Zhao, J., and Wang, Z., (2021), “Effect of the Curing Condition and High-Temperature Exposure on Ground-Granulated Blast-Furnace Slag Cement Concrete”, International Journal of Concrete Structures and Materials, 15 (3), 283-302.
[2]	Aldea, C. M., Young, F., Wang, K., and Shah, S. P. (2000), “Effects of curing conditions on properties of concrete using slag replacement”, Cement and Concrete Research, 30 (3), 465–472.
[3]	Bakharev, T., Sanjayan, J. G., and Cheng, Y.-B. (1999), “Effect of elevated temperature curing on properties of alkali-activated slag concrete”, Cement and Concrete Research, 29 (10), 1619–1625.
[4]	Chini, A. R. (2005), “Effect of elevated curing temperatures on the strength and durability of concrete”, Materials and Structures, 38 (281), 673–679.
[5]	ASTM C09 Committee. (2001), “Practice for making and curing concrete test specimens in the laboratory”, West Conshohocken, PA: ASTM C09 Committee.
[6]	ASTM International. (2001), “Standard test method for compressive strength of cylindrical concrete specimens”, (No. C 39/C 39M – 01). USA: ASTM International.
[7]	Jung, W., and Choi, S.-J., (2017), “Effect of high-temperature curing methods on the compressive strength development of concrete containing high volumes of ground granulated blast-furnace slag”, Advances in Materials Science and Engineering, 1–6.
[8]	Kim T. K., Choi, S. j., Choi, J. H., and Kim, J., (2019), “Prediction of Chloride Penetration Depth Rate and Diffusion Coefficient Rate of Concrete from Curing Condition Variations due to Climate Change Effect”, International Journal of Concrete Structures and Materials, 13 (3), 339-351.
[9]	Kim, T. K., Shin, J. H., Bae, D. H., and Kim, J., (2014), “Performance based evaluation of concrete material properties from climate change effect on wind speed and sunlight exposure time curing condition”, Journal of the Korea Concrete Institute, 26 (6), 751–759.
[10]	Katpady, D. N., Hazehara, H., Soeda, M., Kubota, T., and Murakami, S., (2018), “Durability Assessment of Blended Concrete by Air Permeability”, International Journal of Concrete Structures and Materials, 12 (2), 290-299.
[11]	Halamickova, P., Detwiler, R. J., Bentz, D. P., and Garboczi, E. J., (1995), “Water permeability and chloride ion diffusion in portland cement mortars: relationship to sand content and critical pore diameter”, Cement and Concrete Research, 25 (4), 790–802.
[12]	Sugiyama, T., Bremner, T. W., and Tsuji, Y., (1996), “Determination of chloride diffusion coefficient and gas permeability of concrete and their relationship”, Cement and Concrete Research, 26 (5), 781–790.
[13]	Lee, C., Shin, S. M., Lee, S. H., and Oh, J. H., (2017), “Modeling of Bond Stress–Slip Relationships of a Strand in Concrete during Steam Curing”, International Journal of Concrete Structures and Materials 11 (3), 477–487.
[14]	Roller, J. J., Russell, H. G., Bruce, R. N., and Hassett, B., (2003).”Effect of curing temperatures on high strength concrete bridge girders”, PCI Journal, 48 (2), 72–79.
[15]	ACI 517.2-2R-87, (1992), “Accelerated curing of concrete at atmospheric pressure-state of the art”, Farmington Hills, MI.
[16]	Yi, S. T., Moon, Y. H., and Kim, J. K., (2005), “Long-term strength prediction of concrete with curing temperature”, Cement and Concrete Research, 35 (10), 1961–1969.
[17]	Liu, B., Xie, Y., and Li, J., (2005), “Influence of steam curing on the compressive strength of concrete containing supplementary cementing materials”, Cement and Concrete Research, 35 (5), 994–998.
[18]	Yazici, H., (2007), “The effect of curing conditions on compressive strength of ultra high strength concrete with high volume mineral admixtures”, Building and Environment, 42 (5), 2083–2089.

Cite This Article

Plain Text BibTeX RIS

APA Style

Nam Wook Kim. (2022). Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength. Journal of Civil, Construction and Environmental Engineering, 7(6), 102-108. https://doi.org/10.11648/j.jccee.20220706.11

Copy | Download

ACS Style

Nam Wook Kim. Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength. J. Civ. Constr. Environ. Eng. 2022, 7(6), 102-108. doi: 10.11648/j.jccee.20220706.11

Copy | Download

AMA Style

Nam Wook Kim. Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength. J Civ Constr Environ Eng. 2022;7(6):102-108. doi: 10.11648/j.jccee.20220706.11

Copy | Download

@article{10.11648/j.jccee.20220706.11,
  author = {Nam Wook Kim},
  title = {Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength},
  journal = {Journal of Civil, Construction and Environmental Engineering},
  volume = {7},
  number = {6},
  pages = {102-108},
  doi = {10.11648/j.jccee.20220706.11},
  url = {https://doi.org/10.11648/j.jccee.20220706.11},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.jccee.20220706.11},
  abstract = {The durability of concrete slabs is apt to be influenced by finishing methods and curing methods of concrete surface. Therefore, the finishing agent had better use in case of high strength concrete, the wet curing had better carry out on concrete surface. However, it is not obvious that when wet curing is started after finishing of concrete surface. In this study, the effects of the difference in finishing methods and curing methods on the surface properties of concrete were examined by surface tensile test, air permeability test, water absorption test and scaling test. As a result, use of the finishing agent was effective to improve the surface properties in high strength concrete. However, use of the finishing agent was ineffective in normal strength concrete. When wet curing was carried out, high strength concrete was more effective than normal strength concrete. The surface properties of concrete could be improved when the wet curing was begun after it passed for several hours from finale set of the setting time test for concrete. It is considered that, however, there is not much difference in surface quality within that range, and it is acceptable to start curing water the next day.},
 year = {2022}
}

Copy | Download

TY  - JOUR
T1  - Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength
AU  - Nam Wook Kim
Y1  - 2022/12/08
PY  - 2022
N1  - https://doi.org/10.11648/j.jccee.20220706.11
DO  - 10.11648/j.jccee.20220706.11
T2  - Journal of Civil, Construction and Environmental Engineering
JF  - Journal of Civil, Construction and Environmental Engineering
JO  - Journal of Civil, Construction and Environmental Engineering
SP  - 102
EP  - 108
PB  - Science Publishing Group
SN  - 2637-3890
UR  - https://doi.org/10.11648/j.jccee.20220706.11
AB  - The durability of concrete slabs is apt to be influenced by finishing methods and curing methods of concrete surface. Therefore, the finishing agent had better use in case of high strength concrete, the wet curing had better carry out on concrete surface. However, it is not obvious that when wet curing is started after finishing of concrete surface. In this study, the effects of the difference in finishing methods and curing methods on the surface properties of concrete were examined by surface tensile test, air permeability test, water absorption test and scaling test. As a result, use of the finishing agent was effective to improve the surface properties in high strength concrete. However, use of the finishing agent was ineffective in normal strength concrete. When wet curing was carried out, high strength concrete was more effective than normal strength concrete. The surface properties of concrete could be improved when the wet curing was begun after it passed for several hours from finale set of the setting time test for concrete. It is considered that, however, there is not much difference in surface quality within that range, and it is acceptable to start curing water the next day.
VL  - 7
IS  - 6
ER  -

Copy | Download

Author Information

Nam Wook Kim

Department of Civil and Environmental Engineering, Honam University, Gwangju, Republic of Korea

Download PDF

Sections

Plain Text BibTeX RIS

APA Style

Nam Wook Kim. (2022). Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength. Journal of Civil, Construction and Environmental Engineering, 7(6), 102-108. https://doi.org/10.11648/j.jccee.20220706.11

Copy | Download

ACS Style

Nam Wook Kim. Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength. J. Civ. Constr. Environ. Eng. 2022, 7(6), 102-108. doi: 10.11648/j.jccee.20220706.11

Copy | Download

AMA Style

Nam Wook Kim. Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength. J Civ Constr Environ Eng. 2022;7(6):102-108. doi: 10.11648/j.jccee.20220706.11

Copy | Download

@article{10.11648/j.jccee.20220706.11,
  author = {Nam Wook Kim},
  title = {Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength},
  journal = {Journal of Civil, Construction and Environmental Engineering},
  volume = {7},
  number = {6},
  pages = {102-108},
  doi = {10.11648/j.jccee.20220706.11},
  url = {https://doi.org/10.11648/j.jccee.20220706.11},
  eprint = {https://article.sciencepublishinggroup.com/pdf/10.11648.j.jccee.20220706.11},
  abstract = {The durability of concrete slabs is apt to be influenced by finishing methods and curing methods of concrete surface. Therefore, the finishing agent had better use in case of high strength concrete, the wet curing had better carry out on concrete surface. However, it is not obvious that when wet curing is started after finishing of concrete surface. In this study, the effects of the difference in finishing methods and curing methods on the surface properties of concrete were examined by surface tensile test, air permeability test, water absorption test and scaling test. As a result, use of the finishing agent was effective to improve the surface properties in high strength concrete. However, use of the finishing agent was ineffective in normal strength concrete. When wet curing was carried out, high strength concrete was more effective than normal strength concrete. The surface properties of concrete could be improved when the wet curing was begun after it passed for several hours from finale set of the setting time test for concrete. It is considered that, however, there is not much difference in surface quality within that range, and it is acceptable to start curing water the next day.},
 year = {2022}
}

Copy | Download

TY  - JOUR
T1  - Effects on the Surface Quality of Concrete According to the Changes in the Curing Methods and Compressive Strength
AU  - Nam Wook Kim
Y1  - 2022/12/08
PY  - 2022
N1  - https://doi.org/10.11648/j.jccee.20220706.11
DO  - 10.11648/j.jccee.20220706.11
T2  - Journal of Civil, Construction and Environmental Engineering
JF  - Journal of Civil, Construction and Environmental Engineering
JO  - Journal of Civil, Construction and Environmental Engineering
SP  - 102
EP  - 108
PB  - Science Publishing Group
SN  - 2637-3890
UR  - https://doi.org/10.11648/j.jccee.20220706.11
AB  - The durability of concrete slabs is apt to be influenced by finishing methods and curing methods of concrete surface. Therefore, the finishing agent had better use in case of high strength concrete, the wet curing had better carry out on concrete surface. However, it is not obvious that when wet curing is started after finishing of concrete surface. In this study, the effects of the difference in finishing methods and curing methods on the surface properties of concrete were examined by surface tensile test, air permeability test, water absorption test and scaling test. As a result, use of the finishing agent was effective to improve the surface properties in high strength concrete. However, use of the finishing agent was ineffective in normal strength concrete. When wet curing was carried out, high strength concrete was more effective than normal strength concrete. The surface properties of concrete could be improved when the wet curing was begun after it passed for several hours from finale set of the setting time test for concrete. It is considered that, however, there is not much difference in surface quality within that range, and it is acceptable to start curing water the next day.
VL  - 7
IS  - 6
ER  -

Copy | Download